1.1 This specification covers steel sheet, zinc-coated (galvanized) or zinc-iron alloy-coated (galvannealed) by the hot-dip process in coils and cut lengths.
1.2 The product is produced in various zinc or zinc-iron alloy-coating weights [masses] or coating designations as shown in Table 1 and in Table S2.1.
1.3 Product furnished under this specification shall conform to the applicable requirements of the latest issue of Specification A924/A924M, unless otherwise provided herein.
1.4 The product is available in a number of designations, grades and classes in four general categories that are designed to be compatible with different application requirements.
1.4.1 Steels with mandatory chemical requirements and typical mechanical properties.
1.4.2 Steels with mandatory chemical requirements and mandatory mechanical properties.
1.4.3 Steels with mandatory chemical requirements and mandatory mechanical properties that are achieved through solid-solution or bake hardening.
1.5 This specification is applicable to orders in either inch-pound units (as A653) or SI units (as A653M). Values in inch-pound and SI units are not necessarily equivalent. Within the text, SI units are shown in brackets. Each system shall be used independently of the other.
1.6 The text of this specification references notes and footnotes that provide explanatory material. These notes and footnotes, excluding those in tables and figures, shall not be considered as requirements of this specification.
1.7 Unless the order specifies the “M“ designation (SI units), the product shall be furnished to inch-pound units.
1.8 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use.
TABLE 1 Weight [Mass] of Coating RequirementsA, B, C
Note – Use the information provided in 8.1.3 to obtain the approximate coating thickness from the coating weight [mass].
| Minimum RequirementD | ||||
|---|---|---|---|---|
| Triple-Spot Test (TST) | Single-Spot Test (SST) | |||
| Inch-Pound Units | ||||
| Type | Coating Designation | TST Total Both Sides, oz/ft² |
TST One Side, oz/ft² |
SST Total Both Sides, oz/ft² |
| Zinc | G01 | no minimum | no minimum | no minimum |
| G30 | 0.30 | 0.10 | 0.25 | |
| G40 | 0.40 | 0.12 | 0.30 | |
| G60 | 0.60 | 0.20 | 0.50 | |
| G90 | 0.90 | 0.32 | 0.80 | |
| G100 | 1.00 | 0.36 | 0.90 | |
| G115 | 1.15 | 0.40 | 1.00 | |
| G140 | 1.40 | 0.48 | 1.20 | |
| G165 | 1.65 | 0.56 | 1.40 | |
| G185 | 1.85 | 0.64 | 1.60 | |
| G210 | 2.10 | 0.72 | 1.80 | |
| G235 | 2.35 | 0.80 | 2.00 | |
| G300 | 3.00 | 1.04 | 2.60 | |
| G360 | 3.60 | 1.28 | 3.20 | |
| Zinc-iron alloy | A01 | no minimum | no minimum | no minimum |
| A25 | 0.25 | 0.08 | 0.20 | |
| A40 | 0.40 | 0.12 | 0.30 | |
| A60 | 0.60 | 0.20 | 0.50 | |
| SI Units | ||||
| Type | Coating Designation | TST Total Both Sides, g/m² |
TST One Side, g/m² |
SST Total Both Sides, g/m² |
| Zinc | Z001 | no minimum | no minimum | no minimum |
| Z90 | 90 | 30 | 75 | |
| Z120 | 120 | 36 | 90 | |
| Z180 | 180 | 60 | 150 | |
| Z275 | 275 | 94 | 235 | |
| Z305 | 305 | 110 | 275 | |
| Z350 | 350 | 120 | 300 | |
| Z450 | 450 | 154 | 385 | |
| Z500 | 500 | 170 | 425 | |
| Z550 | 550 | 190 | 475 | |
| Z600 | 600 | 204 | 510 | |
| Z700 | 700 | 238 | 595 | |
| Z900 | 900 | 316 | 790 | |
| Z1100 | 1100 | 390 | 975 | |
| Zinc-iron alloy | ZF001 | no minimum | no minimum | no minimum |
| ZF75 | 75 | 24 | 60 | |
| ZF120 | 120 | 36 | 90 | |
| ZF180 | 180 | 60 | 150 | |
A The coating designation is the term by which the minimum triple spot, total both sides coating weight [mass] is specified. Because of the many variables and changing conditions that are characteristic of continuous hot-dip coating lines, the zinc or zinc-iron alloy coating is not always evenly divided between the two surfaces of a coated sheet; nor is it always evenly distributed from edge to edge. However, the minimum triple-spot average coating weight (mass) on any one side shall not be less than 40 % of the single-spot requirement.
B As it is an established fact that the atmospheric corrosion resistance of zinc or zinc-iron alloy-coated sheet products is a direct function of coating thickness (weight (mass)), the selection of thinner (lighter) coating designations will result in almost linearly reduced corrosion performance of the coating. For example, heavier galvanized coatings perform adequately in bold atmospheric exposure whereas the lighter coatings are often further coated with paint or a similar barrier coating for increased corrosion resistance. Because of this relationship, products carrying the statement “meets ASTM A653/A653Mrequirements“ should also specify the particular coating designation.
C International Standard, ISO 3575, continuous hot-dip zinc-coated carbon steel sheet contains Z100 and Z200 designations and does not specify a ZF75 coating.
D No minimum means that there are no established minimum requirements for triple- and single-spot tests.